CSWIP 3.1 Test 8:
Q. 1/30: Under most circumstances, which of the following do you consider to be duties of a welding inspector?
The supervision of welders.
Procedure writing.
Qualifying welders.
All of the above.
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 1/30
Test Progress : 3.33%
Q. 2/30: A Large grain size in the HAZ of a C-Mn Steel weld joint may have:
Low ductility
Low toughness
High toughness
High tensile strength
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 2/30
Test Progress : 6.67%
Q. 3/30: During CO2 welding, the arc length is most likely to be affected by:
The wire diameter
The current return connections
The gas flow rate
The torch to work angle
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 3/30
Test Progress : 10.00%
Q. 4/30: What is the leg length of a fillet weld?
The distance from the toe to face.
The distance from the root to the toe.
Its 0.7 of the design thickness.
Both b and c
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 4/30
Test Progress : 13.33%
Q. 5/30: Weld Joint in which the parent material and weld metal have significant differences in mechanical properties and/or chemical composition
Homogeneous Joint
Dissimilar Joint
Heterogeneous Joint
All of These
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 5/30
Test Progress : 16.67%
Q. 6/30: What is the leg length of a fillet weld?
The distance from the toe to face.
The distance from the root to the toe.
Its 0.7 of the design thickness.
Both b and c
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 6/30
Test Progress : 20.00%
Q. 7/30: What is the leg length of a fillet weld?
The distance from the toe to face.
The distance from the root to the toe.
Its 0.7 of the design thickness.
Both b and c
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 7/30
Test Progress : 23.33%
Q. 8/30: A typical included angle for MMA welding a full penetration pipe butt joint is:
35º
70º
90º
Dependent on the pipe diameter
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 8/30
Test Progress : 26.67%
Q. 9/30: Incomplete root fusion in a single V butt weld may be caused by:
Linear misalignment
Root gap being too large
Root faces being too small
Welding current too high
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 9/30
Test Progress : 30.00%
Q. 10/30: A WPS may specify a maximum width for individual weld beads (the weave width) when welding C-Mn steels. if the width is exceeded it may cause:
Lack of inter-run fusion
A reduction in HAZ toughness
Lack of sidewall fusion
Too low a deposition rate
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 10/30
Test Progress : 33.33%
Q. 11/30: With reference to the various grades of stainless steels which of the following statements is true?
They are all non-magnetic
They all require 100% Ar for GMAW
They all have very high thermal conductivity
Only certain grades can be used for service at very low temperatures
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 11/30
Test Progress : 36.67%
Q. 12/30: You would certainly recognise a hydrogen controlled flux covered electrode from its
Colour
Length
Trade name
BS639/AWS code letter
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 12/30
Test Progress : 40.00%
Q. 13/30: Incomplete root penetration in a single V butt joint may be caused by:
Excessive root face
Excessive root gap
The current settings being too low
Both a and c
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 13/30
Test Progress : 43.33%
Q. 14/30: According to AWS 2.4 a weld symbol for the other side is placed:
Above the dashed line
Below the dashed line
Above the solid line
Below the solid line
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 14/30
Test Progress : 46.67%
Q. 15/30: Which of following mechanical properties of a weld in carbon manganese steel is most affected if the heat input per unit length of weld is excessively high?
A) Elongation
B) Tensile strength
C) Hardness
D) Toughness
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 15/30
Test Progress : 50.00%
Q. 16/30: Which of the following would be considered to be high heat input welding?
550J/mm
55J/mm
5.5J/mm
5KJ/mm
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 16/30
Test Progress : 53.33%
Q. 17/30: Weld Joint in which the parent material and weld metal have no significant differences in mechanical properties and/or chemical composition
Dissimilar Joint
Homogeneous Joint
Heterogeneous Joint
None Of These
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 17/30
Test Progress : 56.67%
Q. 18/30: Which of the following would be classed as the most serious type of defect?
A buried linear slag inclusion
Buried lack of inter-run fusion
Surface breaking lack of sidewall fusion
Surface porosity
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 18/30
Test Progress : 60.00%
Q. 19/30: Lamellar tearing has occurred in a steel fabrication. Before welding could it have been found by:
Dye penetrant
Ultrasonic inspection
It would not have been found by any inspection method
X-ray examination
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 19/30
Test Progress : 63.33%
Q. 20/30: What is the leg length of a fillet weld?
The distance from the toe to face.
The distance from the root to the toe.
Its 0.7 of the design thickness.
Both b and c
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 20/30
Test Progress : 66.67%
Q. 21/30: A singular gas filled cavity that is= or more than 1.6 mm in diameter is termed?
Cavity
Cluster porosity
Blow hole
Rounded porosity
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 21/30
Test Progress : 70.00%
Q. 22/30: BS EN ISO 5817 (Level B) specifies the limit for excess weld metal (h) on a butt weld as: h<1mm+0.1b, but max. 5mm, b= weld width. In which of the following situations is the measured excess weld metal acceptable?
B = 10 measured excess weld metal = 2.5mm
B = 20 measured excess weld metal = 3.5mm
B = 35 measured excess weld metal = 4.5mm
B = 45 measured excess weld metal = 5.5mm
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 22/30
Test Progress : 73.33%
Q. 23/30: You would certainly recognize a hydrogen controlled flux covered electrode from its:
Color
Length
Trade name
BS639/AWS code letter
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 23/30
Test Progress : 76.67%
Q. 24/30: Which of the following elements is added to steel to give resistance to creep at elevated service temperatures?
Nickel
Manganese
Molybdenum
Aluminium
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 24/30
Test Progress : 80.00%
Q. 25/30: What determines the penetrating power of gammer rays?
Time
Type of isotope
Source-to-film-distance
Source strength
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 25/30
Test Progress : 83.33%
Q. 26/30: One of the reasons for excluding hydrogen from the weld metal is to prevent the weld from:
Cracking
Cooling slowly
Cooling quickly
Expanding
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 26/30
Test Progress : 86.67%
Q. 27/30: For full penetration single-sided butt joints, root bead penetration and profile are mainly influenced by:
Root face
Bevel angle
Root gap
Included angle
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 27/30
Test Progress : 90.00%
Q. 28/30: A qualified Welding Procedure Specification is used to:
Give instruction to the welder
Give information to the welder
Give confidence that welds will have the specified properties.
All of the above
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 28/30
Test Progress : 93.33%
Q. 29/30: The maximum hardness in the HAZ of a steel will increase if the:
Heat input is increased
CEV is increased
Joint thickness is decreased
Basic electrodes are used
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 29/30
Test Progress : 96.67%
Q. 30/30: Welds made with very high heat input will show a reduction in:
Tensile ductility
Notch toughness
Fatigue strength
Creep resistance
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 30/30
Test Progress : 100.00%
Q. 31/30: Preheating a low alloy steel prior to welding to minimise the risk of:
Porosity
Excessive distortion
HAZ cracking
Lack of fusion
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 31/30
Test Progress : 103.33%
.