CSWIP 3.1 Test 6:
Q. 1/30: To test a component for vibrational loading, a suitable mechanical test would be:
Impact
Tensile
Compressive
Fatigue
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 1/30
Test Progress : 3.33%
Q. 2/30: When measuring the welding parameters with the MMA welding process for the purpose of approving a welding procedure, the welding Inspector should measure the voltage:
As close to welding arc as possible.
Anywhere along the welding cable.
Always from the voltmeter on the welding plant.
As near to The welding terminals as possible.
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 2/30
Test Progress : 6.67%
Q. 3/30: When measuring the welding parameters with the MMA welding process for the purpose of approving a welding procedure, the welding Inspector should measure the voltage:
As close to welding arc as possible.
Anywhere along the welding cable.
Always from the voltmeter on the welding plant.
As near to The welding terminals as possible.
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 3/30
Test Progress : 10.00%
Q. 4/30: When measuring the welding parameters with the MMA welding process for the purpose of approving a welding procedure, the welding Inspector should measure the voltage:
As close to welding arc as possible.
Anywhere along the welding cable.
Always from the voltmeter on the welding plant.
As near to The welding terminals as possible.
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 4/30
Test Progress : 13.33%
Q. 5/30: In a bend test, when the face of the specimen is in tension and the root is in compression, the test is called a
Root bend
Side bend
Face bend
Longitudinal bend
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 5/30
Test Progress : 16.67%
Q. 6/30: When visually inspecting the face of a finished weld which of the following flaws would be considered to be the most serious?
Excess weld metal height
Start porosity
Spatter
Arc strikes
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 6/30
Test Progress : 20.00%
Q. 7/30: A Hydrogen controlled MMA electrode can always be recognized by the:
EN code letter (or AWS code number)
Electrode length
Trade name
Colour of the covering
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 7/30
Test Progress : 23.33%
Q. 8/30: Preheating a steel plate with a carbon equivalent (CEV) of 0.48 may be required to:
Drive moisture from the plate
Prevent excessive hardening in the HAZ
Prevent the formation of carbides
Improve the mechanical properties of the weld metal
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 8/30
Test Progress : 26.67%
Q. 9/30: If submerged arc welding is used to make butt welds, which would you be most critical of?
The root gap tolerance
The angle of preparation
The root face width
The gas cut finish
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 9/30
Test Progress : 30.00%
Q. 10/30: In a bend test, when the face of the specimen is in tension and the root is in compression, the test is called a
Root bend
Side bend
Face bend
Longitudinal bend
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 10/30
Test Progress : 33.33%
Q. 11/30: A Fusible insert for TIG welding helps:
Reduce porosity
Give controlled root penetration
Avoid the need for a back purge
By acting as a backing for the root run
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 11/30
Test Progress : 36.67%
Q. 12/30: A fillet weld has an actual throat thickness of 8mm and a leg length of 7mm, what is the excess weld metal?
2.1mm
1.8mm
3.1mm
1.4mm
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 12/30
Test Progress : 40.00%
Q. 13/30: A C-Mn steel is being welded by MMA and the electrode run-out lengths that have been used are much shorter than specified by the WPS. This deviation may give:
Increased risk of hydrogen cracking
Increased risk of solidification cracking
Lower values of HAZ toughness
Higher values of HAZ hardness
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 13/30
Test Progress : 43.33%
Q. 14/30: The tough laminated structure that is formed on slow cooling of ferrite and iron carbide (cementite) is called _______.
Austenite
Martenesite
Pearlite
Trootsite
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 14/30
Test Progress : 46.67%
Q. 15/30: A transverse tensile test from a Weld Procedure Approval Record (WPAR) test plate is used to measure:
Tensile strength of the weld
Tensile strength of the joint
Stress/strain characteristics of the weld
Stress/strain characteristics of the joint
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 15/30
Test Progress : 50.00%
Q. 16/30: When measuring the welding parameters with the MMA welding process for the purpose of approving a welding procedure, the welding Inspector should measure the voltage:
As close to welding arc as possible.
Anywhere along the welding cable.
Always from the voltmeter on the welding plant.
As near to The welding terminals as possible.
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 16/30
Test Progress : 53.33%
Q. 17/30: The first procedure prepared for a Weld Procedure Qualification test is a:
PWPS
WPS
WPQR
WPAR
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 17/30
Test Progress : 56.67%
Q. 18/30: If submerged arc welding is used to make butt welds, which would you be most critical of?
The root gap tolerance
The angle of preparation
The root face width
The gas cut finish
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 18/30
Test Progress : 60.00%
Q. 19/30: What is meant by the term weld junction?
The area containing the HAZ and weld metal.
The weld metal and parent metal.
The boundary between the fusion zone and the HAZ.
The part of the weld which has undergone metallurgical changes due to the heat from welding.
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 19/30
Test Progress : 63.33%
Q. 20/30: Which type of fillet weld is preferred for cyclic loading conditions?
Mitre Type
Convex Type
Concave Type
Any of the above
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 20/30
Test Progress : 66.67%
Q. 21/30: What is meant by the term weld junction?
The area containing the HAZ and weld metal.
The weld metal and parent metal.
The boundary between the fusion zone and the HAZ.
The part of the weld which has undergone metallurgical changes due to the heat from welding.
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 21/30
Test Progress : 70.00%
Q. 22/30: What is meant by the term weld junction?
The area containing the HAZ and weld metal.
The weld metal and parent metal.
The boundary between the fusion zone and the HAZ.
The part of the weld which has undergone metallurgical changes due to the heat from welding.
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 22/30
Test Progress : 73.33%
Q. 23/30: BS EN 970 allows the use of a magnifying glass for visual inspection but recommends that the magnification is:
X2
X2 to x5
X5 to x10
Not greater than x20
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 23/30
Test Progress : 76.67%
Q. 24/30: Incomplete root penetration in a single V butt joint may be caused by:
Excessive root face
Excessive root gap
The current settings being too low
Both a and c
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 24/30
Test Progress : 80.00%
Q. 25/30: A typical temperature range for baking basic coated electrodes is:
150-200ºC
200-250ºC
300-350ºC
400-450ºC
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 25/30
Test Progress : 83.33%
Q. 26/30: Repair welding of in-service plant and equipment may be more difficult than making repairs during initial fabrication because:
The material may be contaminated
Access to repair area may be difficult
Positional welding may be needed
All of the above
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 26/30
Test Progress : 86.67%
Q. 27/30: When TIG welding austenitic stainless steel pipe, argon gas backing is called for. This is to:
Prevent oxidation
Prevent underbead cracking
Prevent porosity
Control the penetration bead shape
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 27/30
Test Progress : 90.00%
Q. 28/30: BS EN 970 allows the use of a magnifying glass for visual inspection but recommends that the magnification is:
X2
X2 to x5
X5 to x10
Not greater than x20
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 28/30
Test Progress : 93.33%
Q. 29/30: A typical temperature range for baking basic coated electrodes is:
150-200ºC
200-250ºC
300-350ºC
400-450ºC
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 29/30
Test Progress : 96.67%
Q. 30/30: If a welding inspector detects a type of imperfection not allowed by the application Standard he must:
Request further NDE
Reject the weld
Prepare a concession request
Reject the weld only is he considers it to be harmful.
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 30/30
Test Progress : 100.00%
Q. 31/30: Preheating a low alloy steel prior to welding to minimise the risk of:
Porosity
Excessive distortion
HAZ cracking
Lack of fusion
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 31/30
Test Progress : 103.33%
.