CSWIP 3.1 Test 3:
Q. 1/30: In an arc welding process, which of the following is the correct term used for the amount of weld metal deposited per minute?
Filling rate.
Deposition rate.
Weld deposition.
Weld duty cycle.
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 1/30
Test Progress : 3.33%
Q. 2/30: The fusion boundary of a fillet weld is the:
Boundary between the weld metal and HAZ
Boundary between individual weld runs
Depth of root penetration
Boundary between HAZ and parent material.
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 2/30
Test Progress : 6.67%
Q. 3/30: The majority of welder qualification tests are carried out using unbacked electrode because:
It is quicker and cheaper if back-gouging is not required.
If the welding process is not TIG. back purging is not required.
All welder qualification tests are done on a small diameter pipe.
It requires more skill and increases the welders' qualification range.
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 3/30
Test Progress : 10.00%
Q. 4/30: The surface of a fatigue crack will:
Be rough and torn
Have sharp chevron markings
Be smooth
Have shear lips
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 4/30
Test Progress : 13.33%
Q. 5/30: BS EN 288 and BS EN ISO 15614 are specifications for?
Welder approval testing
Welding equipment calibration
Welding procedure approval
Consumables for submerged arc welding
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 5/30
Test Progress : 16.67%
Q. 6/30: Bend test specimens have been taken from a 25 mm thick carbon steel butt weld. Which would show lack of inter-run fusion?
Side bend
Root bend
Face bend
Guided bend
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 6/30
Test Progress : 20.00%
Q. 7/30: If a welding inspector detects a type of imperfection not allowed by the application Standard he must:
Request further NDE
Reject the weld
Prepare a concession request
Reject the weld only is he considers it to be harmful.
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 7/30
Test Progress : 23.33%
Q. 8/30: Which of the following electrode types is classified to BS EN 499?
E 38 3 R
E 6013
E 7018 - G
E 51 33 B
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 8/30
Test Progress : 26.67%
Q. 9/30: To improve resistance to service failure caused by cyclic loading, it is good practice to:
Use low heat input welding
Use steel with a low CEV
Ensure there are no features that give high stress concentration
PWHT the fabrication
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 9/30
Test Progress : 30.00%
Q. 10/30: Which of the following AWS A5.1 electrodes has a rutile covering:
E 6010
E 7016
E 7018
E 6013
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 10/30
Test Progress : 33.33%
Q. 11/30: In an arc welding process, which of the following is the correct term used for the amount of weld metal deposited per minute?
Filling rate.
Deposition rate.
Weld deposition.
Weld duty cycle.
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 11/30
Test Progress : 36.67%
Q. 12/30: The risk of hydrogen cracking is greater when MMA welding:
C-Mn Steels
Austenitic Stainless Steels
Low Alloy Steels For Elevated Temperature Service
Low Carbon Steels For Cryogenical Service
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 12/30
Test Progress : 40.00%
Q. 13/30: Lamellar tearing has occurred in a steel fabrication. Before welding could it have been found by:
X-ray examination
Dye penetrant
Ultrasonic examination
It would not have been found by any inspection method
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 13/30
Test Progress : 43.33%
Q. 14/30: Under most conditions which of the following welding positions will deposit the most weld metal.
PG
PE
PC
PA
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 14/30
Test Progress : 46.67%
Q. 15/30: Land is term used with?
J and U joint
Fillet Weld
Single V groove
All of these
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 15/30
Test Progress : 50.00%
Q. 16/30: Under most conditions which of the following welding positions will deposit the most weld metal.
PG
PE
PC
PA
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 16/30
Test Progress : 53.33%
Q. 17/30: Under most conditions which of the following welding positions will deposit the most weld metal.
PG
PE
PC
PA
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 17/30
Test Progress : 56.67%
Q. 18/30: When visually inspecting the root bead of a single V-butt weld it should be checked for:
Lack of root penetration
HAZ hardness
Tungsten inclusions
Slag
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 18/30
Test Progress : 60.00%
Q. 19/30: The strength of a fillet weld is determined by:
Leg length
Weld profile
Weld width
Throat thickness
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 19/30
Test Progress : 63.33%
Q. 20/30: A qualified Welding Procedure Specification is used to:
Give instruction to the welder
Give information to the welder
Give confidence that welds will have the specified properties.
All of the above
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 20/30
Test Progress : 66.67%
Q. 21/30: For radiography of a steel weld at 35mm thickness, the recommended isotope is:
Thulium 170
Ytterbium 169
Iridium 192
Cobalt 60
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 21/30
Test Progress : 70.00%
Q. 22/30: The steel composition in a structural contract is changed from 0.15% carbon 0.6% manganese, to 0.2% carbon 1.2% manganese. This might influence the incidence of:
Porosity
Cracking in the weld area
Undercut for fillet welds
Lack of fusion defects
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 22/30
Test Progress : 73.33%
Q. 23/30: A code of practice is a:
Standard of workmanship quality only
Set of rules for manufacturing a specific product
Specification for the finished product
Code for the qualification of welding procedures and welders qualifications
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 23/30
Test Progress : 76.67%
Q. 24/30: Pipe bores of some materials must be purged with argon before and during TIG welding in order to
Prevent linear porosity
Prevent burn-through
Prevent oxidation of the root bead
Eliminate moisture pick-up in the root bead.
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 24/30
Test Progress : 80.00%
Q. 25/30: A typical included angle for MMA welding a full penetration pipe butt joint is:
35º
70º
90º
Dependent on the pipe diameter
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 25/30
Test Progress : 83.33%
Q. 26/30: The presence of iron sulphides in a weld bead may cause:
Solidification cracking
Hydrogen cracking
Lamellar tearing
Weld decay
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 26/30
Test Progress : 86.67%
Q. 27/30: Z=1.414 x a, this formula is not valid for which type of fillet weld
Mitre type
Convex Type
Concave Type
Valid for all type of fillets
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 27/30
Test Progress : 90.00%
Q. 28/30: When two different material types are welded together the joint is referred to as:
A composite joint
A transition joint
An autogenous weld
Heterogeneous joint
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 28/30
Test Progress : 93.33%
Q. 29/30: Under most conditions which of the following welding positions will deposit the most weld metal.
PG
PE
PC
PA
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 29/30
Test Progress : 96.67%
Q. 30/30: Excess penetration is often caused by which of the following?
Too high a welding current
Slow travel speed
Large root gap
All of the above
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 30/30
Test Progress : 100.00%
Q. 31/30: Which type of SAW flux is susceptible to breaking down into fine particles during circulation?
Fused
Neutral
Alloyed
Agglomerated
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 31/30
Test Progress : 103.33%
.