CSWIP 3.1 Test 12:
Q. 1/30: The strength of a fillet weld is determined by:
Leg length
Weld profile
Weld width
Throat thickness
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 1/30
Test Progress : 3.33%
Q. 2/30: An arc strike (stray flash) on a steel component is regarded by some codes as unacceptable because:
It will cause copper contamination
It may cause hard spots
It may give cracking
Both B and C
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 2/30
Test Progress : 6.67%
Q. 3/30: Which of the following defects is unlikely to be found by visual inspection.
A) Linear misalignment
Undercut
Overlap
D) Linear slag inclusion
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 3/30
Test Progress : 10.00%
Q. 4/30: For MMA welding of a 60mm wall nozzle to a 100mm wall vessel shell, preheat temperatures should be checked:
Before welding starts/restarts
On the shell and nozzle
At points at least 75mm from the joint edge
All of the above
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 4/30
Test Progress : 13.33%
Q. 5/30: A butt joint has how many toes?
2
4
0
1
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 5/30
Test Progress : 16.67%
Q. 6/30: A penertrameter (IQI) is used to measure the:
Size of discontinuity in a weld joint
Density of a radiographic film
Degree of film contrast
Quality of the radiographic technique
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 6/30
Test Progress : 20.00%
Q. 7/30: Proof stress is used when non-ferrous metals are undergoing tensile tests to determine the equivalent Yield strength
True
False
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 7/30
Test Progress : 23.33%
Q. 8/30: Compound welds:
Always contain butt and fillet welds
joints which have combinations of welds made by different welding processes
Combinations between two different weld types
All of the above.
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 8/30
Test Progress : 26.67%
Q. 9/30: What should happen to spatter before visual inspection is carried out?
Spatter is not a problem for visual inspection
Spatter that is more than 2 mm need not be cleaned for visual inspection
Spatter should be cleaned off before visual inspection
Spatter will not have any affect on the weld or the base material
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 9/30
Test Progress : 30.00%
Q. 10/30: A C-Mn steel is being welded by MMA and the electrode run-out lengths that have been used are much shorter than specified by the WPS. This deviation may give:
Increased risk of hydrogen cracking
Increased risk of solidification cracking
Lower values of HAZ toughness
Higher values of HAZ hardness
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 10/30
Test Progress : 33.33%
Q. 11/30: You notice manual metal arc electrodes, stripped of flux, are being used as filler wire for TIG welding. You would object because:
It is too expensive
The wire would be too thick
The metal composition may be wrong
The wire is too short
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 11/30
Test Progress : 36.67%
Q. 12/30: Nick break and fillet fracture tests are used for assessing:
Weld quality
Weld metal ductility
Weld metal toughness
Resistance to fracture
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 12/30
Test Progress : 40.00%
Q. 13/30: Which of the following AWS A5.1 electrodes has a rutile covering:
E 6010
E 7016
E 7018
E 6013
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 13/30
Test Progress : 43.33%
Q. 14/30: Proof stress is used when non-ferrous metals are undergoing tensile tests to determine the equivalent:
Tenacity
Elasticity
Yield strength
Tensile strength
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 14/30
Test Progress : 46.67%
Q. 15/30: The European Standard for NDE of fusion welds by visual examination is:
EN 288
EN 499
EN 287
EN 970
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 15/30
Test Progress : 50.00%
Q. 16/30: According to BS EN 22553 a weld symbol for the other side is placed:
Above the dashed line
Below the dashed line
Above the solid line
Below the solid line
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 16/30
Test Progress : 53.33%
Q. 17/30: A crack running along the centreline of a weld bead could be caused by:
Use of damp flux
Lack of preheat
Arc voltage too high
Weld bead too deep and very narrow
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 17/30
Test Progress : 56.67%
Q. 18/30: Which of the following cutting methods is suitable for cutting stainless steel?
Plasma
Oxy-acetylene
Oxy-propane
It depends upon the thickness.
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 18/30
Test Progress : 60.00%
Q. 19/30: Which physical test is more likely to reveal HAZ embrittlement?
Transverse tensile.
All weld tensile.
Root bend.
Charpy impact.
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 19/30
Test Progress : 63.33%
Q. 20/30: Which of the following procedures would be expected to produce the least distortion in a 15mm straight butt weld?
TIG weld, single-sided, multi-pass
MMA weld, single-sided, multi-pass
MMA weld, double-sided, multi-pass
SAW weld, 1 pass per side
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 20/30
Test Progress : 66.67%
Q. 21/30: The predominant structure of hyper-eutectoid steel that has been quenched at above its upper critical point will be:
Austenite
Martensite
Troostite
Sorbite
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 21/30
Test Progress : 70.00%
Q. 22/30: In the MMA welding process, which of the following is most likely to be caused by a welder with a poor technique?
Deep weld craters/crater cracks.
Copper inclusions
Hydrogen cracks
All of the above
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 22/30
Test Progress : 73.33%
Q. 23/30: For fillet welds it is normal practice in the UK and USA to measure:
Throat thickness
Leg lengths
Penetration depths
Both a and c
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 23/30
Test Progress : 76.67%
Q. 24/30: In the MMA welding process, which of the following is most likely to be caused by a welder with a poor technique?
Deep weld craters/crater cracks.
Copper inclusions
Hydrogen cracks
All of the above
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 24/30
Test Progress : 80.00%
Q. 25/30: In the MMA welding process, which of the following is most likely to be caused by a welder with a poor technique?
Deep weld craters/crater cracks.
Copper inclusions
Hydrogen cracks
All of the above
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 25/30
Test Progress : 83.33%
Q. 26/30: A Fabrication procedure calls for the toes of all welds to be blended in by grinding. The reason for this is to:
Make the weld suitible for liquid (dye) penetrant inspection.
Improve fatigue life.
Reduce residual stresses
Improve the general appearance of the welds
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 26/30
Test Progress : 86.67%
Q. 27/30: Slag inclusions may be present in
Manual metal arc welds
Metal inert gas welds
Metal active gas welds
All welds
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 27/30
Test Progress : 90.00%
Q. 28/30: The chemical composition of the weld metal deposited by a C-Mn steel MMA electrode is usually controlled by:
Core wire composition
Additions in the flux coating
Iron powder in the flux coating
Dilution from the base material
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 28/30
Test Progress : 93.33%
Q. 29/30: The dip transfer or short-circuiting mode of metal transfer used for MIG/MAG welding is characterized by:
Giving deep penetration
Being suitable for positional welding
Giving low spatter
Giving high deposition
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 29/30
Test Progress : 96.67%
Q. 30/30: Preheating for arc welding applies to:
Assembly welding only
Assembly and tack welding
Joints over 25 mm thick only
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 30/30
Test Progress : 100.00%
Q. 31/30: A typical included angle for MMA welding a full penetration pipe butt joint is:
35º
70º
90º
Dependent on the pipe diameter
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 31/30
Test Progress : 103.33%
.