CSWIP 3.1 Test 11:
Q. 1/30: When weld metal refinement takes place in a multi-run deposit, it is known by the term:
Weld annealing
Weld normalising
Weld refining
Weld recrystallisation
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 1/30
Test Progress : 3.33%
Q. 2/30: Lamellar tearing has occurred in a steel fabrication. What technique could have been used to find it before the weld was made?
X-ray examination
Liquid penetrant examination
Ultrasonic examination
It could not have been found by any inspection method
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 2/30
Test Progress : 6.67%
Q. 3/30: Which of the following elements has the greater effect on the hardenability of a steel plate?
Sulphur
Molybdenum
Carbon
Chromium
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 3/30
Test Progress : 10.00%
Q. 4/30: When carrying out visual inspection, the specification makes no mention of the requirements for visual inspection, in this situation what shroud you do?
Carry out normal visual inspection.
Seek advice from higher authority.
Carry out visual inspection.
Re–write the requirements of the specification.
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 4/30
Test Progress : 13.33%
Q. 5/30: A solid inclusion in a weld may be:
Entrapped slag
Entrapped gas
Lack of inter-run fusion
None of the above.
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 5/30
Test Progress : 16.67%
Q. 6/30: When carrying out visual inspection, the specification makes no mention of the requirements for visual inspection, in this situation what shroud you do?
Carry out normal visual inspection.
Seek advice from higher authority.
Carry out visual inspection.
Re–write the requirements of the specification.
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 6/30
Test Progress : 20.00%
Q. 7/30: When carrying out visual inspection, the specification makes no mention of the requirements for visual inspection, in this situation what shroud you do?
Carry out normal visual inspection.
Seek advice from higher authority.
Carry out visual inspection.
Re–write the requirements of the specification.
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 7/30
Test Progress : 23.33%
Q. 8/30: Which group of welders is most likely to require continuous monitoring by a welding inspector?
Concrete shuttering welders
Overland pipeline welders
Tack welders
Maintenance welders
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 8/30
Test Progress : 26.67%
Q. 9/30: In a bend test, when the face of the specimen is in tension and the root is in compression, the test is called a
Root bend
Side bend
Face bend
Longitudinal bend
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 9/30
Test Progress : 30.00%
Q. 10/30: Which type of power source characteristic is normally used for manual welding?
Constant Voltage
Flat Characteristic
Constant Current
A Motor Generator
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 10/30
Test Progress : 33.33%
Q. 11/30: For SAW, what is the effect of raising arc voltage but keeping all other parameters the same?
Weld bead width will increase
Depth of penetration will increase
Weld bead width will decrease
Depth of penetration will decrease
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 11/30
Test Progress : 36.67%
Q. 12/30: A welder qualification test is to verify:
The skill of the welder
The quality of the materials
The non-destructive test procedures
The manufacturing methods
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 12/30
Test Progress : 40.00%
Q. 13/30: Which of the following would be cause for rejection by most fabrication standards when inspecting fillet welds with undercut, a small amount of:
Depth
Length
Width
Sharpness
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 13/30
Test Progress : 43.33%
Q. 14/30: What is the term given for the area of a welded joint outside the weld metal that has undergone microstructural changes?
Heat affected zone.
The weld zone
Fusion zone.
All of the above terms may be used.
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 14/30
Test Progress : 46.67%
Q. 15/30: Nick break and fillet fracture tests are used for assessing:
Weld quality
Weld metal ductility
Weld metal toughness
Resistance to fracture
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 15/30
Test Progress : 50.00%
Q. 16/30: Typical temperature used for normalising a C-Mn steel plate are:
600-650ºC
1000-1100ºC
700-800ºC
880-920ºC
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 16/30
Test Progress : 53.33%
Q. 17/30: With reference to the various grades of stainless steels which of the following statements is true?
They are all non-magnetic
They all require 100% Ar for GMAW
They all have very high thermal conductivity
Only certain grades can be used for service at very low temperatures
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 17/30
Test Progress : 56.67%
Q. 18/30: A welder qualification test is to verify:
The quality of the materials
The non-destructive test procedures
The skill of the welder
The manufacturing methods
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 18/30
Test Progress : 60.00%
Q. 19/30: When carrying out visual inspection, the specification makes no mention of the requirements for visual inspection, in this situation what shroud you do?
Carry out normal visual inspection.
Seek advice from higher authority.
Carry out visual inspection.
Re–write the requirements of the specification.
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 19/30
Test Progress : 63.33%
Q. 20/30: Initiation of a TIG arc using high frequency spark may not be allowed because it:
Often causes tungsten inclusions
Can damage electronic equipment
Is an electrical safety hazard
Often causes stop/start porosity
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 20/30
Test Progress : 66.67%
Q. 21/30: A fabricating procedure calls for fillet welds to be 'blended in' by grinding. This influences:
HAZ. cracking
Fatigue life
Residual stress
Yield strength
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 21/30
Test Progress : 70.00%
Q. 22/30: Compound welds:
Always contain butt and fillet welds
joints which have combinations of welds made by different welding processes
Combinations between two different weld types
All of the above.
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 22/30
Test Progress : 73.33%
Q. 23/30: The Boundary between the weld metal and HAZ
Weld Zone
Weld Junction
Haz
None Of these
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 23/30
Test Progress : 76.67%
Q. 24/30: Compound welds:
Always contain butt and fillet welds
joints which have combinations of welds made by different welding processes
Combinations between two different weld types
All of the above.
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 24/30
Test Progress : 80.00%
Q. 25/30: Compound welds:
Always contain butt and fillet welds
joints which have combinations of welds made by different welding processes
Combinations between two different weld types
All of the above.
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 25/30
Test Progress : 83.33%
Q. 26/30: The European Standard for NDE of fusion welds by visual examination is:
EN 288
EN 499
EN 287
EN 970
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 26/30
Test Progress : 86.67%
Q. 27/30: When visually inspecting the root bead of a single V-butt weld it should be checked for:
Lack of root penetration
HAZ hardness
Tungsten inclusions
Slag
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 27/30
Test Progress : 90.00%
Q. 28/30: If welding travel speed is doubled but the current and voltage remain the same the heat input will be:
Reduced by 50%
Increased by a factor of two
About the same
Reduced by approximately 25%
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 28/30
Test Progress : 93.33%
Q. 29/30: The temperature range over which a steel goes from having high to low toughness is called the:
Critical transformation temperature
Ductility dip temperature
Bi-modal temperature
Transition temperature
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 29/30
Test Progress : 96.67%
Q. 30/30: You notice manual metal arc electrodes, stripped of flux, are being used as filler wire for TIG welding. You would object because:
It is too expensive
The wire would be too thick
The metal composition may be wrong
The wire is too short
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 30/30
Test Progress : 100.00%
Q. 31/30: The strength of a fillet weld is determined by:
Leg length
Weld profile
Weld width
Throat thickness
Please select an option and click submit.
.
Your answer is correct. Welldone! Click next.
Sorry, your answer is incorrect. Click next.
Submit
Previous
Next
Q 31/30
Test Progress : 103.33%
.
Select another Test